2mm CR Stainless Steel Sheet AISI 304 316L ASTM A240 Decroate SS Plate
Grade 304 Stainless Steel
The melting point of 304 stainless steel is higher than its 316 stainless steel counterpart,
ranging between 2,550 – 2,650 °F or 1399 – 1454 °C. But as the material draws closer to these
temperatures, it continues to lose its tensile strength gradually.
Product introduction:
| Commodity | 2mm CR Stainless Steel Sheet AISI 304 316L ASTM A240 Decroate SS Plate |
| Grade | 304 316L |
| Brand | TISCO ,BAOSTEEL,POSCO,JISCO,LISCO |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 2 mm |
| Width | 1000 mm,1219 mm,1500 mm as per customers’ requirements |
| Length | 2000, 3000, 6000 mm or as per customers’ requirements |
| Surface | 2B; No.4; Mirror |
| Standard | JIS,AISI,ASTM,GB,DIN |
| Delivery time | About 15 -30 days or based on the sales contract |
| MOQ | 1 Ton |
| Advantages | offers higher creep, stress to rupture and tensile strength at elevated temperatures. |
Grade 316L:
The L denotes the low content of carbon in the steel. 316L is best known among fabricators for being resistant to cracks after the weld process is completed. This makes 316L the preferred choice of fabricators who look to build metallic structures for industry applications.
316L is the superior choice for high corrosion and high temperature applications. Since 316L contains less carbon than 316, it has better intergranular corrosion resistance, meaning its welds won't decay, unlike with 316 stainless steel.
Chemical Composition:
| Grade | C | Si | Mn | P | S | Ni | Cr | Mo |
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00～10.00 | 18.00～20.00 | - |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 12.00～15.00 | 16.00～18.00 | 2.00～3.00 |
Physical Property:
| Grade | Tensile Strength(Mpa) | Yield Strength(Mpa) | Elongation(%) | HBW | HRB | HV |
| 304 | ≥520 | ≥205 | ≥40 | ≤187 | ≤90 | ≤200 |
| 316L | ≥480 | ≥175 | ≥40 | ≤187 | ≤90 | ≤200 |
Surface Finish:
| Surface Finish | Definition | Application |
| 2B | Finished by heat treatment, pickling after cold rolling. Followed by skin pass line to be more brighter and smooth surface | General application Medical instruments, Tableware |
| BA | Bright heat treament after cold rolling | Kitchen utensil, kitchenware, architectural |
| 8K | A mirror-like reflective surface by polishing with finer abrasives over 800mesh | Construction, mirrors, plate sets, decoration elevators |
| HL | Finished by continuous linear polishing | Architectural purpose, Escalators, kitchenware, vehicles |
| NO.1 | Finished by hot rolling, annealing and picking, characterized by white pickled surface | Chemical industry Equipment, industrail tanks |
| NO.4 | Polishing with NO.150 to NO.180 mesh abrasives specified in JISR6001 | Kitchen utensils, Building Construction, Medical equipment |
Packing: